Interfacial biomechanical properties of a dual acid-etched versus a chemically modified hydrophilic dual acid-etched implant surface: an experimental study in Beagles

International Journal of Implant Dentistry volume 4, Article number: 28 (2018) Cite this article

Abstract

Background

The high survival clinical success rates of osseointegration are requisites for establishing a long-term biomechanical fixation and load-bearing potential of endosseous oral implants. The objective of this preclinical animal study was to evaluate the effect of surface microtopography and chemistry on the early stages of biomechanical rigidity with a sandblasted, dual acid-etched surface, with or without an additional chemical modification (SAE-HD and SAE, respectively), in the tibia of Beagle dogs.

Methods

Two pairs of implants, with the same macrogeometry but different surface technology ((a) dual acid-etched surface treatment with hydrochloric and sulfuric acid followed by microwave treatment and insertion in isotonic saline solution to increase hydrophilicity (SAE-HD) (test, n = 12) and (b) dual acid-etched surface (SAE) (control, n = 12)), were installed bilaterally in the proximal tibia of six Beagle dogs. In order to determine the effect of surface modification on biomechanical fixation, a test protocol was established to assess the torque and a complete set of intrinsic properties. Maximum removal torque (in N cm) was the primary outcome measure, while connection stiffness (N cm/rad) and removal energy (× 10−2J) were the secondary outcome measures and were assessed after 2 and 4 weeks in vivo. A general linear statistical model was used and performed for significant differences with the one-way ANOVA followed by Tukey post hoc test (P < 0.05).

Results

The removal torque values did not reveal significant statistical differences between SAE-HD and SAE implants at any observation times (P = 0.06). Although a slight increase over time could be observed in both test and control groups. SAE-HD showed higher removal energy at 4 weeks (999.35 ± 924.94 × 10− 2 J) compared to that at 2 weeks (421.94 ± 450.58 × 10− 2 J), while SAE displayed lower values at the respective healing periods (P = 0.16). Regarding connection stiffness, there were no significant statistical differences neither within the groups nor over time. There was a strong, positive monotonic correlation between removal torque and removal energy (=0.722, n = 19, P < 0.001).

Conclusions

In this study, no significant differences were observed between the specific hydrophilic (SAE-HD) and hydrophobic (SAE) surfaces evaluated, in terms of biomechanical properties during the early osseointegration period.

Background

The progressive evolution of oral implant surface technology (i.e., micro to nanotopography and chemical composition) [1, 2], implant macrogeometry, surgical procedures [3,4,5], and loading protocols [6,7,8] has resulted in high survival and clinical success rates [9]. Accordingly, chemically active micro and nanostructured implant surfaces, presenting moderate surface roughness (Ra/Sa values between 1 and 2 μm), enhance host-to-implant interactions [10,11,12] and have been shown to shorten the period needed for time-critical functional implant loading (i.e., so-called immediate or early loading) [13,14,15].

Recent in vitro analyses support the concept that hydrophilic surfaces upregulate the expression of angiogenic factors, activate the production of anti-inflammatory factors, and downregulate the expression of pro-inflammatory cytokines by osteoblasts [16] and macrophage-like cells [17, 18], and regulate osteogenic differentiation and maturation of mesenchymal stem cells (MSCs) [10, 19, 20] and human osteoblast-like cells [21,22,23], increasing osteogenesis and decreasing osteoclastogenesis [11, 23, 24]. Furthermore, higher surface energy and hydrophilicity is demonstrated to induce faster bone-to-implant contact (%BIC) and bone density, both in preclinical in vivo experiments [25,26,27] and in patients [7, 28, 29]. Indeed, higher biomechanical stability as expression of primary and secondary bone anchorage is recorded following hydrophilic implant placement [26, 30].

Particularly, a superhydrophilic moderately rough titanium (Ti) implant surface (contact angle less than 5°) has been suggested to play a critical role during the early healing period [27] and establishment of a successful osseointegration [31] in preclinical in vivo studies. The microarchitecture and density of the trabecular bone formed around oral implants, characterized by a high ratio of metabolic activity and remodeling, is one of the main determinants of interfacial shear strength, mechanical resistance, and adaptation to overloading stress [32]. The potential of chemically modified superhydrophilic implant surfaces to enhance osteogenic differentiation and increase early bone apposition onto the implant may shorten the implant stability drop, occurring due to bone remodeling during the first few weeks of implantation [13]. Consequently, such microstructured surface technology may lessen the healing (non-loading) period and allow more readily immediate or early functional implant loading in patients with reduced bone density. Nevertheless, there is lack of knowledge regarding the intrinsic biomechanical aspects of osseointegration related to this specific implant surface technology (i.e., removal torque, removal energy, and connection stiffness) during the initial osseointegration process.

Evaluation of biological effects and biomechanical properties of innovative technologies in the field of implant dentistry in preclinical animal models, prior to translational research, complies with standard regulations [33]. Thus, the aim of this preclinical animal study was to evaluate the effect of surface microtopography and chemistry on the biomechanical properties of implants with a sandblasted, dual acid-etched surface, with or without an additional chemical modification (SAE-HDFootnote 1 and SAE,Footnote 2 respectively), during the early stages of osseointegration in the tibia of Beagle dogs. Specifically, we hypothesized that a chemically active implant surface presenting superhydrophilicity generates higher interfacial shear strength in comparison to a hydrophobic surface, expressed as higher maximum removal torque, removal energy, and connection stiffness.

Methods

The present preclinical in vivo study is reported according to the Animal Research: Reporting of In Vivo Experiments (ARRIVE) guidelines, in regard with relevant items [33]. The animal experimental protocol was approved by the Bioethics Committee for Animal Experimentation (CEUA, protocol no. 098/10) at the Federal University of Uberlândia and followed the normative guidelines of the National Council for Animal Control and Experimentation (CONCEA), constituent of the Ministry of Science, Technology and Innovation (MCTI), Law no. 11.794, 08/19/2008, Brazil. The in vivo part of the study was conducted between November 2012 and January 2013.

Experimental units

Twenty-four commercially pure Ti implants (10 mm × 4 mm, L × Ø) with a moderately rough surface, produced by means of sandblasting and dual acid-etching with hydrochloric and sulfuric acid were used in the present study. Implants in the control group were only sandblasted and dual acid-etched (SAE; n = 12). In the test group, after sandblasting and dual acid etching, implants received proprietary technology treatment, including microwave treatment and insertion in isotonic saline solution resulting in significantly increased hydrophilicity (SAE-HD; n = 12). These specific implant surfaces exhibit the following 3D surface roughness parameters for SAE and SAE-HD, respectively: Sa 1.44 μm ± 1.15 and 1.26 μm ± 0.17; Sz 14.57 μm ± 1 and 16.20 μm ± 7.8; Sdr 1.51 and 1.21%; Sds 658.67 1/mm2 ± 27.42 and 643.33 1/mm2 ± 37.74; and Ssk −0.51 and −0.43 [27]. The chemical composition of the different surfaces was examined by X-ray photoelectron spectroscopy (XPS). The atomic percentage values of carbon were 49 and 17, and 22 and 59 of oxygen in SAE and SAE-HD groups, respectively. The surface energy and wettability was investigated by means of a static contact angle analysis by means of the sessile drop technique [34] applying simulated body fluid (SBF) solution. SAE-HD disks reveal a superhydrophilic behavior (contact angle < 5°), whereas SAE surfaces display superhydrophobic properties (contact angle > 90°).

The implants present similar macrodesign with an external hexagon connection system and cylindrical body containing double triangular threads with high potential for bone compression recommended for type III and IV bone, commercially available as Titamax Ti Ex®. Neodent®Footnote 3 supplied all implants.

Animal model

Six male Beagle dogs (~ 1.5 years old), weighting between 13 and 15 kg, were used in the present study. All animals were acclimatized in the experimental animal care facility of Federal University of Uberlândia for 2 weeks previously to the experimental procedures and randomly pair-housed in standard shelters (1 × 1.5 m kennel) to allow environmental enrichment (i.e., variety of toys, daily group play sessions, resistance running, and training) at the ambient temperature of 22 °C, under controlled humidity and 12-h circadian rhythm. The diet consisted of hard pellet and water ad libitum. The animal caretakers were blind to the experimental groups. The level of pain, distress, or suffering was daily assessed during the observation period to ensure the welfare of the animals. Aiming to guarantee selection blindness during the experimental allocation, the groups were systematically coded by a third person and the first implant to be placed in each tibia was randomly assigned. Sample size was calculated based on information in previous studies using the dog tibia model to allow evaluation of possible differences in bone-to-implant contact between groups. The surgical procedures and the histological/histomorphometrical outcomes of the study have been reported elsewhere [31].

Briefly, two pairs of implants (10 mm × 4 mm, L × Ø) from each of the experimental groups were placed under copious sterile saline irrigation and with a torque of about 45 N cm (last drill 3.5 mm Ø) in each proximal tibia of the animals (total no. of implants 48). Implants were placed with an alternating fashion in terms of medio-distal positioning with the first group chosen at random and surgeries were staged between left and right tibia to provide 2 and 4 weeks of healing times, i.e., 12 implants per group and per observation time. The first implant was inserted ca. 2 cm below the femoral-tibial-patellar joint line at the central medial-lateral portion of the proximal tibiae (Fig. 1). The following implants were placed in a distal direction with inter-implant distances of 1 cm along the central region of the bone until the tibia patellar joint. Implants were furnished with cover screws and then soft tissues were sutured in layers for primary intention healing. Postoperative pain and infection control was provided for 7 days. The animals were euthanized under sedation with an anesthesia overdose, and the upper third of the tibias was retrieved. The specimens were fixed in 10% buffered formalin solution and half of them were allocated to histomorphometric analysis and the other half to biomechanical analysis, reported herein.

Fig. 1
figure 1

Two pairs of implants (10 mm × 4 mm, L × Ø) from each of the experimental groups were placed in each tibia with an alternating fashion in terms of medio-distal positioning regarding the group, but with the first group chosen at random. Implants were placed with an inter-implant distance of 1 cm

Full size image

Assessment of interfacial biomechanical properties

To assess the biomechanical strength of the bone-implant interface, the following parameters were assessed: (a) maximum removal torque (N cm) (primary outcome measure), obtained during the unscrewing process (primary outcome measure); (b) connection stiffness (N cm/rad), corresponding to the ratio between removal torque and angular displacement (secondary outcome measure); and (c) removal energy (× 10–2 J), corresponding to the energy (workload) necessary to completely unscrew the implant (secondary outcome measure).

The removal torque test was conducted on a Shimadzu universal testing machine.Footnote 4 This equipment was adapted in order to determine the referred properties (Fig. 2a, b). A horizontal shaft, supported by two ball bearings, with Allen keys socket on one end and a rotation sensor on the other end, was connected with a steel string to the mobile span of the Shimadzu universal testing machine, in such a way that the linear motion was converted to a rotational motion. The dog’s tibia bone block containing the implant was placed in alignment and inside the Allen keys socket and fixed with an adjustable clamp, in order not to rotate during the test. The upper span speed, at which the string was attached, was adjusted to produce a shaft rotation speed of 0.005 rad/s. During the test, both torque (N cm) and angular displacement (rad) were acquired using a sampling rate of 10 samples/s (Fig. 3a, b). In order to calculate the connection stiffness (N cm/rad), the tangent method was applied to the data after obtaining the linear correlation coefficient (R2) compared to the secant method, revealing the absence of mathematical discrepancy between the application of both methods (Fig. 4).

Fig. 2
figure 2

Adaptation of Shimadzu universal testing machine for performing removal torque test of dental implants. a General view. b Assembly detail of connection between Allen keys socket and the implant placed in the tibia

Full size image
Fig. 3
figure 3

Representative curve of the torque test for implants. a Graph of torque versus angular displacement with linear regression curve, and equation, representing the connection stiffness. b Determination procedure of unscrewing implant work up to test’s maximum torque

Full size image
Fig. 4
figure 4

Comparison among secant and tangent methods to calculate the connection stiffness values, which reveals the absence of mathematical discrepancy

Full size image

Calibration of one blinded examiner (R.N.R.J) and repeated measurements for data reproducibility was performed under supervision and prior to performing the removal torque test and respective calculation of connection stiffness.

Statistical analysis

A general linear statistical model with torque, energy, and stiffness as dependent variables and implant surface and time in vivo as independent variables was used at 95% level of significance and performed by one-way ANOVA followed by Tukey’s post hoc test. The Spearman rank correlation test was taken in order to test the association concerning the investigated dependent variables. Since sample size calculation, as already mentioned, was made to allow evaluation of possible differences in bone-to-implant contact between groups, a post hoc analysis was performed to define the minimum detectable difference between groups regarding the parameters assessed herein, with a power of 80% and an alpha error of 0.05%. The IBM® SPSS® Statistics softwareFootnote 5 was used.

Results

No remarkable events were observed during the surgical procedures and the subsequent healing period. The relative biomechanical performance of both experimental implant surfaces is illustrated in a representative graph of removal torque versus angular displacement. The removal torque, removal energy, and connection stiffness values are described in terms of mean, standard deviation, and 95% confidence interval for mean in Fig. 5. The results of one-way ANOVA variance and Tukey’s post hoc test values of the variables for SAE-HD and SAE implant at 2 and 4 weeks postoperatively (n = 6) are demonstrated in Table 1.

Fig. 5
figure 5

Mean and standard deviation of the biomechanical data at both observation periods (P > 0.05). a Removal torque. b Removal energy. c Connection stiffness

Full size image
Table 1 One-way ANOVA variance and Tukey’s post hoc test values of removal torque (N cm), removal energy [N cm/rad (0.01 J)], and connection stiffness [N cm/rad] for SAE-HD and SAE implants at 2 and 4 weeks postoperatively (n = 6; P < 0.05)
Full size table

The removal torque values (N cm) did not reveal significant statistical differences between SAE-HD and SAE implants at any observation period (P = 0.06), but a slight increase over time could be observed in both test and control groups (Fig. 5a). Removal torque at 2 weeks was 60.18 ± 24.12 and 54.00 ± 29.91 N cm, and at 4 weeks was 88.11 ± 14.96 and 79.05 ± 14.59 N cm for SAE-HD and SAE implants, respectively (Fig. 5b). SAE-HD showed higher removal energy [J] at 4 weeks (9.99 ± 9.25) compared to 2 weeks (4.22 ± 4.50), while SAE displayed lower values at corresponding healing times (5.21 ± 1.49 vs. 2.83 ± 2.49, respectively) (P = 0.16). Regarding connection stiffness (N cm/rad), SAE showed lower values at 2 weeks (462.57 ± 507.75) compared with 4 weeks of healing (689.01 ± 496.28), however not statistically significant (Fig. 5c). SAE-HD disclosed similar results at 2 and 4 weeks (652.98 ± 111.26 vs. 661.56 ± 369.28, respectively) without statistically significant differences neither between the groups, nor over time (P = 0.76).

A Spearman’s correlation test was run to determine the connection between maximum removal torque, removal energy, and connection stiffness values (Table 2) during the interfacial strength assessment. There was a strong, positive monotonic correlation between removal torque and removal energy (=0.722, n = 19, P < 0.001). However, there was no evidence of positive correlation between removal torque and connection stiffness (=0.352, n = 24, P = 0.092). Moreover, a negative correlation between removal energy and connection stiffness was observed (=− 0.91, n = 19, P = 0.710).

Table 2 Spearman rank correlation coefficient values between removal torque (N cm), removal energy [N cm/rad (0.01 J)], and connection stiffness [N cm/rad] for SAE-HD and SAE implants at 2 and 4 weeks postoperatively (n = 6; P < 0.01)
Full size table

Discussion

Improving surface wettability aims to increase the implant surface area achieving most favorable protein adsorption and cellular adhesion and thereby to positively regulate the biological response at the initial osseointegration process. Thus, the superior potential of superhydrophilic surfaces in enhancing osseointegration at early stages of bone formation may also enhance their load-bearing capacity and biomechanical resistance.

In the present study, both SAE-HD implants and SAE implants showed relatively high amounts of maximum removal torque values at both observation times. In contrast, the SAE-HD implants showed relatively high values in removal energy compared with SAE implants at both 2 and 4 weeks. Specifically, the test group presented consistently higher values (about 100% higher) in removal energy compared with the control group at both observation times. Further, SAE-HD implants showed high values in connection stiffness already after 2 weeks of healing, while SAE implants required 4 weeks of healing to reach a similar level. Thus, despite the fact that the differences between the two groups were not significant for any of the evaluated parameters or observation times, the results seem to indicate that differences in surface properties between SAE-HD and SAE implants, somehow influenced osseointegration and intrinsic properties of shear strength. Indeed, greater removal torque values and interfacial stiffness for hydrophilic implants (modSLA)1 between 2 and 4 weeks, in comparison with SLA2, have been previously reported [35]. In this study [35], performed in the anterior maxilla of miniature pigs, hydrophilic implants revealed, on average, 8–21 and 9–14% significantly higher removal torque and interfacial stiffness values, respectively, than those of the SLA implants. Due to the remodeling process, the biomechanical parameters decreased with time for both implant surfaces, reflecting the developing biological stability.

It has been previously reported the existence of a correlation between removal torque and %BIC values [26], although the nature of these parameters differs from one another (three-dimensional versus most often two-dimensional parameter) [36]. Indeed, the lack of differences between the groups herein reflect well the results of the histomorphometric analysis of the other half of implants in the present study, reported elsewhere [31]. In particular, similar amounts of osseointegration in terms of %BIC and bone density were observed in both groups (SAE-HD vs. SAE) at each observation time, and there were no statistically significant differences regarding the respective parameters between the two observations times [31]. In contrast, Sartoretto et al. [27] demonstrated that Acqua® implants (Neodent®), which present similar technology as the SAE-HD implants, resulted in accelerated osseointegration when placed in tibia of rabbits after 2 weeks of healing, compared with implants with the Neoporos® surface, which in turn presents similar technology with the SAE surface. The difference between the study of de Jesus et al. [31] and Sartoretto et al. [27] in terms of the impact of surface technology on histomorphometric osseointegration parameters may be due to anatomical and/or biological differences in the experimental models employed. In this context, although there is no scientific support regarding the optimal experimental model to evaluate aspects of osseointegration, the dog is one of the most commonly used animal platforms [36]. The mandible of dogs is the most frequent location; however, a high percentage of studies on implant integration have used extra-oral implant sites, including the tibia [37]. It is suggested that due to its anatomy, with a large lumen and relatively low trabecular density [38], it possesses high discriminating potential regarding the impact of implant surface technologies to enhance osseointegration. Furthermore, the tibia allows placement of a larger number of implants comparing with the mandible, thus allowing the use of fewer animals and/or multiple types of comparisons/tests (e.g., biomechanical and histological evaluation).

On the other hand, lack of significant differences between the two groups in the present experiment could be due to the fact that the effect of hydrophilicity, in terms of accelerating bone healing and osseointegration, was unfolded before the first evaluation time-point of 2 weeks, i.e., during the very early healing period. Consistently, pre-clinical investigations show the potential of chemically modified surfaces to rapidly modulate the host-to-implant response upon prompt adsorption of blood proteins [20, 22]. In a recent study reported by Vasak et al. [39], hydrophilic implants (SLActivea) strengthened the apposition of newly formed bone at the very early healing period between 5 and 10 days in the intra-oral model of minipigs, even though they did not reveal significant statistical differences in comparison to hydrophobic surfaces (SLA). Clinically, a systematic review of human histological studies on molecular aspects of osseointegration [29] has shown that moderately rough implant surfaces with high hydrophilicity enhance molecular processes related to osseointegration during the early stages of wound healing. Similar clinical studies assessed the degree of new bone-to-implant contact (%NBIC) around SLActive implants in comparison to SLA placed in the mandibular retromolar region in man during the early stages of osseointegration [28, 40]. The authors reported a progressive increase in %NBIC around both implants, whereas chemically active surfaces disclosed higher values at 2 and 4 weeks compared with SLA, no longer observed after 6 weeks of osseointegration.

Studies including biomechanical analysis of osseointegration are usually assessing maximum removal torque. Although this parameter is important, use of a single parameter appears not sufficient for a complete biomechanical assessment of osseointegration. Herein, connection stiffness, reflecting the rigidity (i.e., the stability of the implant under load), and removal energy, reflecting the overall energy (workload) necessary to loosen the bone-to-implant connection, were additionally assessed. It is suggested that the use of these three parameters in a complementary manner is essential for complete evaluation of the biomechanical properties of implants. Indeed, two different osseointegrated implants can have the same maximum removal torque, but distinct connection stiffness; similarly, they may show the same removal energy but perform in a very distinct fashion and show distinct connection stiffness and maximum removal torque. To the best of the authors’ knowledge, this is the first original research reporting removal energy as an intrinsic removal torque property in relation to connection stiffness during biomechanical assessment of hydrophilic implants; however, removal energy has already been used assessing mini-implants with hydrophobic surfaces [41].

In fact, the observed lack of differences between the groups could be attributed to the relatively low number of specimens per group. According to the observed data herein, applying a high power (80%) with the present sample size would had revealed a relatively large difference in removal torque equivalent to 43% between the experimental groups. Regarding removal energy and connection stiffness, this difference would had been equal to 71 and 34%, respectively. In addition, a significant difference may not had been achieved due to the nature of the specimens. Biological material properties vary greatly from organism to organism and even in the same animal. Therefore, in future studies when using the presented methodology, a greater number of specimens must be considered. This will evidence a superior discrimination capacity. Nonetheless, the current methodology is far more reliable than the use of a single parameter methodology.

Conclusions

No significant differences were observed between the specific hydrophilic (SAE-HD) and hydrophobic (SAE) surfaces evaluated in this study, in terms of biomechanical properties during the early osseointegration period.

Notes

  1. Chemically modified sandblasted, large grit, and acid-etched surfaces

  2. Sandblasted, large grit, and acid-etched surfaces

  3. Neodent, Rua Benjamin Lins, 742, Curitiba, PR 80420–100, Brazil

  4. Shimadzu Corporation, Nishinokyo Kuwabara-cho, Nakagyo-ku, Kyoto 604–8511, Japan

  5. IBM Corporation v.23, 1 New Orchard Road, Armonk, New York 10, 504–1722, USA

References

  1. Cochran DL, Jackson JM, Jones AA, Jones JD, Kaiser DA, Taylor TD, et al. A 5-year prospective multicenter clinical trial of non-submerged dental implants with a titanium plasma-sprayed surface in 200 patients. J Periodontol. 2011;82(7):990–9. https://doi.org/10.1902/jop.2011.100464.

    Article  PubMed  Google Scholar 

  2. Wallkamm B, Ciocco M, Ettlin D, Syfrig B, Abbott W, Listrom R, et al. Three-year outcomes of Straumann Bone Level SLActive dental implants in daily dental practice: a prospective non-interventional study. Quintessence Int. 2015;46(7):591–602. https://doi.org/10.3290/j.qi.a34076.

    PubMed  Google Scholar 

  3. Baires-Campos FE, Jimbo R, Bonfante EA, Fonseca-Oliveira MT, Moura C, Zanetta-Barbosa D, et al. Drilling dimension effects in early stages of osseointegration and implant stability in a canine model. Med Oral Patol Oral Cir Bucal. 2015;20(4):471–9.

    Article  Google Scholar 

  4. Blanco J, Alvarez E, Munoz F, Linares A, Cantalapiedra A. Influence on early osseointegration of dental implants installed with two different drilling protocols: a histomorphometric study in rabbit. Clin Oral Implants Res. 2011;22(1):92–9. https://doi.org/10.1111/j.1600-0501.2010.02009.

    Article  PubMed  Google Scholar 

  5. Jimbo R, Tovar N, Anchieta RB, Machado LS, Marin C, Teixeira HS, et al. The combined effects of undersized drilling and implant macrogeometry on bone healing around dental implants: an experimental study. Int J Oral Maxillofac Surg. 2014;43(10):1269–75. https://doi.org/10.1016/j.ijom.2014.03.017.

    Article  PubMed  Google Scholar 

  6. Marković A, Čolić S, Šćepanović M, Mišić T, Ðinić A, Bhusal DS. A 1-year prospective clinical and radiographic study of early-loaded bone level implants in the posterior maxilla. Clin Implant Dent Relat Res. 2015;17(5):1004–13. https://doi.org/10.1111/cid.12201.

    Article  PubMed  Google Scholar 

  7. Nicolau P, Korostoff J, Ganeles J, Jackowski J, Krafft T, Neves M, et al. Immediate and early loading of chemically modified implants in posterior jaws: 3-year results from a prospective randomized multicenter study. Clin Implant Dent Relat Res. 2013;15(4):600–12. https://doi.org/10.1111/j.1708-8208.2011.00418.

    Article  PubMed  Google Scholar 

  8. Romanos G, Grizas E, Laukart E, Nentwig GH. Effects of early moderate loading on implant stability: a retrospective investigation of 634 implants with platform switching and Morse-tapered connections. Clin Implant Dent Relat Res. 2016;18(2):301–9. https://doi.org/10.1111/cid.12314.

    Article  PubMed  Google Scholar 

  9. Karabuda ZC, Abdel-Haq J, Arιsan V. Stability, marginal bone loss and survival of standard and modified sand-blasted, acid-etched implants in bilateral edentulous spaces: a prospective 15-month evaluation. Clin Oral Implants Res. 2011;22(8):840–9. https://doi.org/10.1111/j.1600-0501.2010.02065.

    Article  PubMed  Google Scholar 

  10. Wall I, Donos N, Carlqvist K, Jones F, Brett P. Modified titanium surfaces promote accelerated osteogenic differentiation of mesenchymal stromal cells in vitro. Bone. 2009;45(1):17–26. https://doi.org/10.1016/j.bone.2009.03.662.

    Article  PubMed  Google Scholar 

  11. Mamalis AA, Markopoulou C, Vrotsos I, Koutsilirieris M. Chemical modification of an implant surface increases osteogenesis and simultaneously reduces osteoclastogenesis: an in vitro study. Clin Oral Implants Res. 2011;22(6):619–26. https://doi.org/10.1111/j.1600-0501.2010.02027.

    Article  PubMed  Google Scholar 

  12. Lotz EM, Olivares-Nasarrete R, Berner S, Boyan BD, Schwartz Z. Osteogenic response of human MSCs and osteoblasts to hydrophilic and hydrophobic nanostructured titanium implant surfaces. J Biomed Mater Res A. 2016;104(12):3137–48. https://doi.org/10.1002/jbm.a.35852.

    Article  PubMed  Google Scholar 

  13. Chambrone L, Shibli JA, Mercurio CE, Cardoso B, Preshaw PM. Efficacy of standard (SLA) and modified sandblasted and acid-etched (SLActive) dental implants in promoting immediate and/or early occlusal loading protocols: a systematic review of prospective studies. Clin Oral Implants Res. 2015;26(4):359–70. https://doi.org/10.1111/clr.12347.

    Article  PubMed  Google Scholar 

  14. Heinemann F, Hasan I, Bourauel C, Biffar R, Mundt T. Bone stability around dental implants: treatment related factors. Ann Anat. 2015;199:3–8. https://doi.org/10.1016/j.aanat.2015.02.004.

    Article  PubMed  Google Scholar 

  15. Hinkle RM, Rimer SR, Morgan MH, Zeman P. Loading of titanium implants with hydrophilic endosteal surface 3 weeks after insertion: clinical and radiological outcome of a 12-month prospective clinical trial. J Oral Maxillofac Surg. 2014;72(8):1495–502. https://doi.org/10.1016/j.joms.2014.04.016.

    Article  PubMed  Google Scholar 

  16. Hyzy SL, Olivares-Navarrete R, Hutton DL, Tan C, Boyan BD, Schwartz Z. Microstructured titanium regulates interleukin production by osteoblasts, an effect modulated by exogenous BMP-2. Acta Biomater. 2013;9(3):5821–9. https://doi.org/10.1016/j.actbio.2012.10.030.

    Article  PubMed  Google Scholar 

  17. Hamlet S, Alfarsi M, George R, Ivanovski S. The effect of hydrophilic titanium surface modification on macrophage inflammatory cytokine gene expression. Clin Oral Implants Res. 2012;23(5):584–90. https://doi.org/10.1111/j.1600-0501.2011.02325.

    Article  PubMed  Google Scholar 

  18. Hotchkiss KM, Ayad NB, Hyzy SL, Boyan BD, Olivares-Navarrete R. Dental implant surface chemistry and energy alter macrophage activation in vitro. Clin Oral Implants Res. 2017;28(4):414–23. https://doi.org/10.1111/clr.12814.

    Article  PubMed  Google Scholar 

  19. Rosa AL, Kato RB, Castro Raucci LMS, Teixeira LN, de Oliveira FS, Bellesini LS, et al. Nanotopography drives stem cell fate toward osteoblast differentiation through α1β1 integrin signaling pathway. J Cell Biochem. 2014;115(3):540–8. https://doi.org/10.1002/jcb.24688.

    Article  PubMed  Google Scholar 

  20. Boyan BD, Cheng A, Olivares-Navarrete R, Schwartz Z. Implant surface design regulates mesenchymal stem cell differentiation and maturation. Adv Dent Res. 2016;28(1):10–7. https://doi.org/10.1177/0022034515624444.

    Article  PubMed  PubMed Central  Google Scholar 

  21. Mamalis AA, Silvestros SS. Analysis of osteoblastic gene expression in the early human mesenchymal cell response to a chemically modified implant surface: an in vitro study. Clin Oral Implants Res. 2011;22(5):530–7. https://doi.org/10.1111/j.1600-0501.2010.02049.

    Article  PubMed  Google Scholar 

  22. Kato RB, Roy B, De Oliveira FS, Ferraz EP, De Oliveira PT, Kemper AG, et al. Nanotopography directs mesenchymal stem cells to osteoblast lineage through regulation of microRNA-SMAD-BMP-2 circuit. J Cell Physiol. 2014;229(11):1690–6. https://doi.org/10.1002/jcp.24614.

    Article  PubMed  PubMed Central  Google Scholar 

  23. Zhao G, Schwartz Z, Wieland M, Rupp F, Geis-Gerstorfer J, Cochran DL, et al. High surface energy enhances cell response to titanium substrate microstructure. J Biomed Mater Res A. 2005;74((1):49–58. https://doi.org/10.1002/jbm.a.30320.

    Article  Google Scholar 

  24. Bang SM, Moon HJ, Kwon YD, Yoo JY, Pae A, Kwon IK. Osteoblastic and osteoclastic differentiation on SLA and hydrophilic modified SLA titanium surfaces. Clin Oral Implants Res. 2014;25(7):831–7. https://doi.org/10.1111/clr.12146.

    Article  PubMed  Google Scholar 

  25. Buser D, Broggini N, Wieland M, Schenk RK, Denzer AJ, Cochran DL, et al. Enhanced bone apposition to a chemically modified SLA titanium surface. J Dent Res. 2004;83(7):529–33. https://doi.org/10.1177/154405910408300704.

    Article  PubMed  Google Scholar 

  26. Gottlow J, Barkarmo S, Sennerby L. An experimental comparison of two different clinically used implant designs and surfaces. Clin Implant Dent Relat Res. 2012;14(Suppl 1):204–12. https://doi.org/10.1111/j.1708-8208.2012.00439.

    Article  Google Scholar 

  27. Sartoretto SC, Alves AT, Resende RF, Calasans-Maia J, Granjeiro JM, Calasans-Maia MD. Early osseointegration driven by the surface chemistry and wettability of dental implants. J Appl Oral Sci. 2015;23(3):279–87. https://doi.org/10.1590/1678-775720140483.

    Article  PubMed  PubMed Central  Google Scholar 

  28. Lang NP, Salvi GE, Huynh-Ba G, Ivanovski S, Donos N, Bosshardt DD. Early osseointegration to hydrophilic and hydrophobic implant surfaces in humans. Clin Oral Implants Res. 2011;22(4):349–56. https://doi.org/10.1111/j.1600-0501.2011.02172.

    Article  PubMed  Google Scholar 

  29. Shanbhag S, Shanbhag V, Stavropoulos A. Genomic analyses of early peri-implant bone healing in humans: a systematic review. Int J Implant Dent. 2015;1(1):5. https://doi.org/10.1186/s40729-015-0006-2.

    Article  PubMed  PubMed Central  Google Scholar 

  30. Guler AU, Sumer M, Duran I, Sandikci EO, Telcioglu NT. Resonance frequency analysis of 208 Straumann dental implants during the healing period. J Oral Implantol. 2013;39(2):161–7. https://doi.org/10.1563/AAID-JOI-D-11-00060.

    Article  PubMed  Google Scholar 

  31. de Jesus RNR, Stavropoulos A, Oliveira MTF, Soares PBF, Moura CCG, Zanetta-Barbosa D. Histomorphometric evaluation of a dual acid-etched vs. a chemically modified hydrophilic dual acid-etched implant surface. An experimental study in dogs. Clin Oral Implants Res. 2017;28(5):551–7. https://doi.org/10.1111/clr.12833.

    Article  PubMed  Google Scholar 

  32. Frost HM. Skeletal structural adaptations to mechanical usage (SATMU): 1. Redefining Wolff’s law: the bone modeling problem. Anat Rec. 1990;226(4):403–13.

    Article  PubMed  Google Scholar 

  33. Berglundh T, Stavropoulos A; Working Group 1 of the VIII European Workshop on Periodontology. Preclinical in vivo research in implant dentistry. Consensus of the eighth European workshop on periodontology J Clin Periodontol 2012;39 Suppl 12:1–5. doi: https://doi.org/10.1111/j.1600-051X.2011.01827.

  34. Sawase T, Jimbo R, Baba K, Shibata Y, Ikeda T, Atsuta M. Photo-induced hydrophilicity enhances initial cell behavior and early bone apposition. Clin Oral Implants Res. 2008;19(5):491–6. https://doi.org/10.1111/j.1600-0501.2007.01509.

    Article  PubMed  Google Scholar 

  35. Ferguson SJ, Broggini N, Wieland M, de Wild M, Rupp F, Geis-Gerstorfer J, et al. Biomechanical evaluation of the interfacial strength of a chemically modified sandblasted and acid-etched titanium surface. J Biomed Mater Res A. 2006;78((2):291–7. https://doi.org/10.1002/jbm.a.30678.

    Article  Google Scholar 

  36. Marin C, Granato R, Suzuki M, Gil JN, Piattelli A, Coelho PG. Removal torque and histomorphometric evaluation of bioceramic grit-blasted/acid-etched and dual acid-etched implant surfaces: an experimental study in dogs. J Periodontol. 2008;79(10):1942–9. https://doi.org/10.1902/jop.2008.080106.

    Article  PubMed  Google Scholar 

  37. Stadlinger B, Pourmand P, Locher MC, Schulz MC. Systematic review of animal models for the study of implant integration, assessing the influence of material, surface and design. J Clin Periodontol. 2012;39(Suppl 12):28–36. https://doi.org/10.1111/j.1600-051X.2011.01835.

    Article  PubMed  Google Scholar 

  38. Pearce AI, Richards RG, Milz S, Schneider E, Pearce SG. Animal models for implant biomaterial research in bone: a review. Eur Cell Mater. 2007;13:1):1–10.

    Article  PubMed  Google Scholar 

  39. Vasak C, Busenlechner D, Schwarze UY, Leitner HF, Munoz Guzon F, Hefti T, et al. Early bone apposition to hydrophilic and hydrophobic titanium implant surfaces: a histologic and histomorphometric study in minipigs. Clin Oral Implants Res. 2014;25(12):1378–85. https://doi.org/10.1111/clr.12277.

    Article  PubMed  Google Scholar 

  40. Bosshardt DD, Salvi GE, Huynh-Ba G, Ivanovski S, Donos N, Lang NP. The role of bone debris in early healing adjacent to hydrophilic and hydrophobic implant surfaces in man. Clin Oral Implants Res. 2011;22(4):357–64. https://doi.org/10.1111/j.1600-0501.2010.02107.

    Article  PubMed  Google Scholar 

  41. Kim S, Lee S, Cho I, Kim S, Kim T. Rotational resistance of surface-treated mini-implants. Angle Orthod. 2009;79(5):899–907. https://doi.org/10.2319/090608-466.1.

    Article  PubMed  Google Scholar 

Download references

Acknowledgements

The assistance of fifth-year dental students of the Federal University of Uberlândia in surgeries, including auscultation, and other practicalities is highly appreciated.

Funding

The Brazilian Federal Agency for Support and Evaluation of Graduate Education (CAPES research fellow, Full PhD Program, process no. 0975-14.1) provided funding and Neodent® (Curitiba, PR, Brazil) produced the titanium implants. None of the funding institutions influenced the study design and data collection, analysis, and interpretation or the manuscript writing process.

Availability of data and materials

The datasets used and/or analyzed during the current study are available from the corresponding author on reasonable request.

Author information

Authors and Affiliations

  1. Department of Periodontology, Faculty of Odontology, Malmö University, Carl Gustafs väg 34, 205-06, Malmö, Sweden

    Rainde Naiara Rezende de Jesus & Andreas Stavropoulos

  2. IBILI, Faculty of Medicine, University of Coimbra, Av. Bissaya Barreto, Bloco de Celas, 3000-075, Coimbra, Portugal

    Rainde Naiara Rezende de Jesus & Eunice Carrilho

  3. CEMUC, Mechanical Engineering Department, University of Coimbra, Pinhal de Marrocos, 3030-788, Coimbra, Portugal

    Pedro V. Antunes & Amílcar Ramalho

  4. Department of Endodontics, Faculty of Odontology, Federal University of Uberlândia, Av Pará 1720, Bloco4LB, Campus Umuarama, Uberlândia, Minas Gerais, 38405-900, Brazil

    Camilla Christian Gomes Moura

  5. Department of Oral and Maxillofacial Surgery and Implantology, Faculty of Odontology, Federal University of Uberlândia, Av Pará 1720, Bloco4LB, Campus Umuarama, Uberlândia, Minas Gerais, 38405-900, Brazil

    Darceny Zanetta-Barbosa

Authors
  1. Rainde Naiara Rezende de Jesus
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Eunice Carrilho
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Pedro V. Antunes
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Amílcar Ramalho
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Camilla Christian Gomes Moura
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Andreas Stavropoulos
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Darceny Zanetta-Barbosa
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

RNRJ participated in the study concept and design and performed the animal operations, biomechanical test, and data analysis and interpretation. EC, PVA, and AR contributed to define the test protocol and performed the biomechanical test and data analysis. CCGM and DZ participated in the study concept and design and performed the animal operations and data analysis. AS contributed to data analysis, interpretation, and drafting of the manuscript. All authors have contributed to and/or critically revised the manuscript and given approval to the final version of the manuscript.

Corresponding author

Correspondence to Andreas Stavropoulos.

Ethics declarations

Ethics approval

The animal experimental protocol was approved by the Bioethics Committee for Animal Experimentation (CEUA, protocol no. 098/10) at the Federal University of Uberlândia.

Competing interests

Rainde Naiara Rezende de Jesus, Eunice Carrilho, Pedro V. Antunes, Amílcar Ramalho, Camilla Christian Gomes Moura, Andreas Stavropoulos, and Darceny Zanetta-Barbosa declare that they have no competing interests.

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

de Jesus, R.N.R., Carrilho, E., Antunes, P.V. et al. Interfacial biomechanical properties of a dual acid-etched versus a chemically modified hydrophilic dual acid-etched implant surface: an experimental study in Beagles. Int J Implant Dent 4, 28 (2018). https://doi.org/10.1186/s40729-018-0139-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s40729-018-0139-1

Keywords