The influence of implant–abutment connection on the screw loosening and microleakage
© The Author(s). 2018
- Received: 20 November 2017
- Accepted: 24 January 2018
- Published: 9 April 2018
There are some spaces between abutment and implant body which can be a reservoir of toxic substance, and they can penetrate into subgingival space from microgap at the implant–abutment interface. This penetration may cause periimplantitis which is known to be one of the most important factors associated with late failure. In the present study, three kinds of abutment connection system, external parallel connection (EP), internal parallel connection (IP), and internal conical connection (CC), were studied from the viewpoint of microleakage from the gap between the implant and the abutment and in connection with the loosening of abutment screw.
We observed dye leakage from abutment screw hole to outside through microgap under the excessive compressive and tensile load and evaluated the anti-leakage characteristics of these connection systems.
During the experiment, one abutment screw for EP and two screws for IP, out of seven samples in each group, were fractured. After the 2000 cycles of compressive tensile loadings, removal torque value (RTV) of abutment screw represented no statistical differences among three groups. Standard deviation was largest in the RTV of EP and smallest in that of CC. The results of microleakage of toluidine blue from implant–abutment connection indicated that microleakage generally increased as loading procedure progressed.
The amount of microleakage was almost plateau at 2000 cycles in CC, but still increasing in other two groups. The value of microleakage greatly scattered in EP, but the deviation of that in CC is significantly smaller. At 500 cycles of loading, there were no significant differences in the amount of microleakage among the groups, but at 1000, 1500, and 2000 cycles of loading, the amount of microleakage in CC was significantly smaller than that in IP. Throughout the experiment, the amount of microleakage in EP was largest, but no statistical difference was indicated due to the high standard deviation.
Within the limitation of the present study, CC was stable even after the loading in the RTV of abutment screw and it prevented microleakage from the microgap between the implant body and the abutment, among the three tested connections.
- Implant–abutment connection
- Screw loosening
- Toluidine blue
- Non-axial load
Although promising outcome of implant therapy has been reported, periimplantitis which is known to be one of the most important factors associated with late failure  is a serious complication and expected to overcome to obtain successful outcome. It is known that there are some spaces between abutment and implant body which can be a reservoir of microorganisms and other toxic substance , and they can penetrate into subgingival space from microgap located at the implant–abutment interface. This is believed to impact to periimplant inflammation . Thus, many kinds of implant–abutment connection have been proposed to minimize the microgap .
Implant–abutment connection can be divided into three types, external parallel connection (EP), internal parallel connection (IP), and conical connection which has the friction between the implant and the abutment (CC). Nobel Biocare has implant systems with these three kinds of implant–abutment connections, and these connection systems are popular even in other manufacturers and they also employ one or some of these connection systems. These systems have a lot of pros and cons and should be selected depending on the dentists’ demand.
In the present study, we would like to consider these three kinds of connection system from the point of view of microleakage from the gap between the implant and the abutment and in connection with the loosening of abutment screw. We herewith performed the investigation of dye leakage from abutment screw hole to outside through microgap under the excessive cyclic load applied to cantilever superstructure. Cantilever model could simulate non-axial offset loading applied to implant–abutment complex, and toluidine blue solution was used to measure the extravasation from the gap at the implant–abutment interface.
This assembly was set in a universal test machine (Autograph AS-1S, Shimadzu, Kyoto, Japan), and load was applied to the cantilever, at 17.5 mm distance from the center of access hole.
As one cycle, one compressive and tensile loads (10 N each) was applied per 1 s and 2000 cycles of loading was done. Before starting load application and every 100 cycles, 100 μl solutions were collected from pool and absorbance at 627 nm was measured using a spectrophotometer (Biospec-mini, Shimadzu). Every 500 cycles, the amount of microleakage was statistically compared using Student t test with Bonferroni correction for multiple comparisons. After the completion of 2000-cycle loading, removal torque value (RTV) of abutment screw was measured.
During the experiment, one (EP) and two (IP) abutment screws out of seven samples were fractured. In this case, abutment screw was changed to new one and experimental procedure was re-run.
RTV of abutment screw after 2000-cycle loading
Microleakage of toluidine blue from implant–abutment connection
In the present study, cyclic tensile and compressive loading were applied to cantilever superstructure. In the clinical situation, both compressive and tensile force was exerted to implant-supported prosthesis, but no previous study has discussed the microleakage using model study under this situation. In case of conical connection, compressive force may have promoted a higher penetration of the abutments into implant body, which may eliminate microgap . But in the clinical situation, tensile force may also be applied to abutment–implant interface as indicated above; the model employed in the present study may be pertinent.
Some previous model studies which measured the extent of microleakage from implant–abutment interface employed microorganisms [6–9]. These studies focused on bacteria itself using visible solution cloudiness test , scanning electron microscopy , bacteria viability test , or checkerboard DNA–DNA hybridization method  and did not mentioned about the bacterial toxin. Toluidine blue employed in the present study can easily be measured using absorptiometry and it was reported to be similar to bacterial toxins in its molecular size . In addition, trend in microleakage was reportedly similar between bacterial leakage model and dye leakage model .
In the present study, removal toque of abutment screw after the cyclic loading showed no statistically significant difference among the groups. Generally, conical abutment is believed to be better in fit and stability than non-conical connection . One possibility of this discrepancy may be due to the deformation of abutment screw. Actually, implant–abutment connection after the removal of abutment screw was still tight in CC group, but they were easily divided in other two groups. This may indicate that implant–abutment connection in CC group was almost sound and intact after the loading. In contrast, in EP and IP groups, abutment screw may be deformed which lead to the increase of RTV of abutment screw. The fracture of abutment screws in EP and IP groups may support this speculation. In addition, axial force is strongly affected by the interfacial friction coefficient . In the present study, interfacial friction was supposed to be largest in CC group because the contact area between implant body and abutment was smallest in EP group and both EP and IP groups had parallel walls at the interface with gaps and voids [13, 14]. This may be one reason for the larger standard deviation of RTV in both EP and IP groups.
In the present study, chronological increase of the amount of microleakage was observed in all three groups. This is in consistent with previous studies [5, 13, 15, 16]. Sigmoid curves of microleakage in all groups meant that the amount of leakage was large at the early stage of loading. This was in agreement with previous reports. Harder et al. reported that bacterial toxin leak occurred within 5 min of incubation using in vitro experimental model study, even without application of loading [15, 16].
The comparison of microleakage among the groups at every 500-cycle load indicated that there were no significant differences among the groups at 500-cycle loading but were statistically significant differences in those between IP and CC groups. The reason for microleakage in EP group having no significant differences indicated between EP and IP or CC groups may be due to the largeness of standard deviation in the value of EP group.
The limitation of the present study was the number of samples. We believed the sample number (seven in each group) was sufficient to obtain the trends of microleakage, but it may be better to investigate using large number of samples to analyze the nature of microleakage at the implant–abutment interface in detail. Another limitation was that the fastening torque applied to screw was not necessarily accurate. To mimic clinical situation, we used dedicated beam-type toque wrench delivered from manufacturer. According to the previous studies, the wrench of Nobel Biocare only reportedly demonstrated the target torque value falling within the 95% confidence interval for the true population mean among four kinds of wrenches . In addition, significantly lower deviations of torque values for beam-type wrenches were reported than for coil and toggle-style wrenches . But toque wrench still has an inaccuracy because the scale printed on the wrench is not fine and it seems to be inappropriate to apply precise torque value. In the present study, we used new torque wrench, but in the clinical settings, variability of toque value may expand because torque wrench is repeatedly used, with sterilization procedure, which decrease the accuracy .
Within the limitation of the present study, after the offset cyclic tensile and compressive loading, the amount of microleakage from implant–abutment interface was smaller in conical connection than in internal parallel connection.
The experiment was done by self-funding.
YA contributed to the establishment of the concept of this work, data acquisition and analysis, drafting the paper, and final approval of the work. KT contributed to the establishment of the concept of this work, data acquisition and analysis, drafting the paper, and final approval of the work. TM contributed to the data acquisition and analysis, drafting the paper, and final approval of the work. MK contributed to the data acquisition and analysis, drafting the paper, and final approval of the work. KK contributed to the data acquisition and analysis, drafting the paper, and final approval of the work.
The present study was not required ethical approval.
Katsuhiro Tsuruta, Yasunori Ayukawa, Tatsuya Matsuzaki, Masafumi Kihara, and Kiyoshi Koyano declare that they have no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
- Sakka S, Baroudi K, Nassani MZ. Factors associated with early and late failure of dental implants. J Investig Clin Dent. 2012;3:258–61.View ArticlePubMedGoogle Scholar
- Tallarico M, Canullo L, Caneva M, Ozcan M. Microbial colonization at the implant-abutment interface and its possible influence on periimplantitis: a systematic review and meta-analysis. J Prosthodont Res. 2017;61:233–41.View ArticlePubMedGoogle Scholar
- Sasada Y, Cochran DL. Implant-abutment connections: a review of biologic consequences and peri-implantitis implications. Int J Oral Maxillofac Implants. 2017;32:1296–307.View ArticlePubMedGoogle Scholar
- Liu Y, Wang J. Influences of microgap and micromotion of implant-abutment interface on marginal bone loss around implant neck. Arch Oral Biol. 2017;83:153–60.View ArticlePubMedGoogle Scholar
- da Silva-Neto JP, Prudente MS, Dantas TS, Senna PM, Ribeiro RF, das Neves FD. Microleakage at different implant-abutment connections under unloaded and loaded conditions. Implant Dent. 2017;26:388–92.View ArticlePubMedGoogle Scholar
- Aloise JP, Curcio R, Laporta MZ, Rossi L, da Silva AM, Rapoport A. Microbial leakage through the implant-abutment interface of Morse taper implants in vitro. Clin Oral Implants Res. 2010;21:328–35.View ArticlePubMedGoogle Scholar
- Dibart S, Warbington M, Su MF, Skobe Z. In vitro evaluation of the implant-abutment bacterial seal: the locking taper system. Int J Oral Maxillofac Implants. 2005;20:732–7.PubMedGoogle Scholar
- Silva-Neto JP, Prudente MS, Carneiro Tde A, Nobilo MA, Penatti MP, Neves FD. Micro-leakage at the implant-abutment interface with different tightening torques in vitro. J Appl Oral Sci. 2012;20:581–7.View ArticlePubMedPubMed CentralGoogle Scholar
- do Nascimento C, Barbosa RE, Issa JP, Watanabe E, Ito IY, de Albuquerque Junior RF. Use of checkerboard DNA-DNA hybridization to evaluate the internal contamination of dental implants and comparison of bacterial leakage with cast or pre-machined abutments. Clin Oral Implants Res. 2009;20:571–7.View ArticlePubMedGoogle Scholar
- Piattelli A, Scarano A, Paolantonio M, Assenza B, Leghissa GC, Di Bonaventura G, et al. Fluids and microbial penetration in the internal part of cement-retained versus screw-retained implant-abutment connections. J Periodontol. 2001;72:1146–50.View ArticlePubMedGoogle Scholar
- Schmitt CM, Nogueira-Filho G, Tenenbaum HC, Lai JY, Brito C, Doring H, et al. Performance of conical abutment (Morse Taper) connection implants: a systematic review. J Biomed Mater Res A. 2014;102:552–74.View ArticlePubMedGoogle Scholar
- Egol KA, Kubiak EN, Fulkerson E, Kummer FJ, Koval KJ. Biomechanics of locked plates and screws. J Orthop Trauma. 2004;18:488–93.View ArticlePubMedGoogle Scholar
- Tsuge T, Hagiwara Y, Matsumura H. Marginal fit and microgaps of implant-abutment interface with internal anti-rotation configuration. Dent Mater J. 2008;27:29–34.View ArticlePubMedGoogle Scholar
- Scarano A, Valbonetti L, Degidi M, Pecci R, Piattelli A, de Oliveira PS, et al. Implant-abutment contact surfaces and microgap measurements of different implant connections under 3-dimensional X-ray microtomography. Implant Dent. 2016;25:656–62.View ArticlePubMedGoogle Scholar
- Harder S, Dimaczek B, Acil Y, Terheyden H, Freitag-Wolf S, Kern M. Molecular leakage at implant-abutment connection—in vitro investigation of tightness of internal conical implant-abutment connections against endotoxin penetration. Clin Oral Investig. 2010;14:427–32.View ArticlePubMedGoogle Scholar
- Harder S, Quabius ES, Ossenkop L, Kern M. Assessment of lipopolysaccharide microleakage at conical implant-abutment connections. Clin Oral Investig. 2012;16:1377–84.View ArticlePubMedGoogle Scholar
- Britton-Vidal E, Baker P, Mettenburg D, Pannu DS, Looney SW, Londono J, et al. Accuracy and precision of as-received implant torque wrenches. J Prosthet Dent. 2014;112:811–6.View ArticlePubMedGoogle Scholar
- Neugebauer J, Petermoller S, Scheer M, Happe A, Faber FJ, Zoeller JE. Comparison of design and torque measurements of various manual wrenches. Int J Oral Maxillofac Implants. 2015;30:526–33.View ArticlePubMedGoogle Scholar
- Stroosnijder E, Gresnigt MM, Meisberger EW, Cune MS. Loss of accuracy of torque wrenches due to clinical use and cleaning procedure: short communication. Int J Prosthodont. 2016;29:253–5.View ArticlePubMedGoogle Scholar