In vitro comparison of two titanium dental implant surface treatments: 3M™ESPE™ MDIs versus Ankylos®
International Journal of Implant Dentistry volume 3, Article number: 27 (2017)
An ideal implant should have a surface that is conducive to osseointegration. In vitro cell culture studies using disks made of same materials and surface as of implants may provide useful information on the events occurring at the implant-tissue interface. In the current study, we tested the hypothesis that there is no difference in the proliferation and differentiation capacities of osteoblastic cells when cultured on titanium disks mimicking the surface of 3M™ESPE™ MDIs or standard (Ankylos®) implants.
Cells were grown on disks made of the same materials and with same surface texture as those of the original implants. Disks were sterilized and coated with 2% gelatin solution prior to the cell culture experiments. C2C12 pluripotent cells treated with 300 ng/ml bone morphogenetic protein 2 BMP-2 and a stably transfected C2C12 cell line expressing BMP2 were used as models for osteogenic cells. The Hoechst 33258-stained nuclei were counted to assay cell proliferation, while alkaline phosphatase (ALPL) immunostaining was performed to investigate osteogenic differentiation. MC3T3-E1 cells were cultured as model osteoblasts. The cells were differentiated and assayed for proliferation and metabolic activities by Hoechst 33258 staining and Alamar blue reduction assays, respectively. Additionally, cultures were stained by calcein to investigate their mineral deposition properties.
Electron microscopy showed greater degree of roughness on the MDI surfaces. Nuclear counting showed significantly higher number of C2C12 cells on the MDI surface. Although immunostaining detected higher number of ALPL-positive cells, it was not significant when normalized by cell numbers. The number of MC3T3-E1 cells was also higher on the MDI surface, and accordingly, these cultures showed higher Alamar blue reduction. Finally, calcein staining revealed that the MC3T3-E1 cells grown on MDI surfaces deposited more minerals.
Although both implant surfaces are conducive for osteoblastic cell attachment, proliferation, and extracellular matrix mineralization, cell proliferation is higher on MDI surfaces, which may in turn facilitate osseointegration via increased ECM mineralization.
Prosthetic devices are often used as surrogates for missing skeletal and dental elements. These devices are in close contact with the surrounding tissues, and their functionality and stability are critically dependent on the successful integration within the tissue’s extracellular matrix (ECM). The surface of the implanted device directly interacts with cell and extracellular milieu and influences their biological activities affecting the healing of the implant site after the surgery, tissue regeneration, and the formation of an organic interface with cells and ECM proteins.
Dental implants are commonly used to replace missing teeth, and the long-term success of these implants depends on their proper integration with the mineralized bone, a process commonly known as osseointegration .
It has been a long-standing challenge to achieve successful osseointegration of implants in older population with poor bone mass and low bone turnover rates. Therefore, an ideal implant should have a surface which is conducive to osseointegration regardless of the implant site, bone quality, and bone quantity. A large body of literature recommends the use of mini dental implants for stabilization of removable partial and complete dentures in selected situations .The 3M™ESPE™ mini dental implant (MDI) system makes use of a self-tapping threaded screw design and needs a minimal surgical intervention. Also, small-size implants have been widely used for orthodontic anchorage [3,4,5], single tooth replacements [6, 7], fixing the surgical guides for definitive implant placement , and as transitional implants for the support of interim removable prosthesis during the healing phase of final fixtures [9, 10]. The MDIs have several advantages over the regular implants used for overdentures such as, simpler surgical protocol and minimally invasive surgery, and they can often be loaded immediately . This helps in reducing postoperative distress to the patient and minimizing resorption of the bone during healing . It has been shown that bone healing around immediately loaded transitional implants is not disturbed and causes no bone loss, which represents a solution for patients who have ridge deficiency and who cannot have surgery for medical reasons [12, 13]. Mini dental implants are also cost-effective, and the price of one MDI is 3.5 times lower than that of a standard size mandibular implant .
Despite the advantages of the MDI, evidence on their potential for osseointegration and long-term success is lacking. [15,16,17,18]. Newer implant systems entering the market must be studied first in vitro and then in vivo with animal models followed by human studies to demonstrate their osseointegration capability.
Modifications of implant surface properties have been shown to have a positive influence on the successful osseointegration of an implant [19,20,21,22]. Surface properties such as roughness, topography, and chemistry are strongly related to the biocompatibility of implants . Thus, modulation of these properties can be useful means to improve implant osseointegration in patients with poor bone quality. The most common treatments used for implant surface modifications are acid etching and sandblasting [24,25,26,27]. Implants with moderate surface coarseness demonstrate a better bone response than a smoother or rougher surface [28,29,30]. When an implant is placed in the bone, a series of cell and matrix events takes place. These mainly include host response to the implant material and behavior of the implant in the host tissue, which culminates in an intimate deposition of a new bone on the implant surface .
The immediate event after implantation is adsorption of proteins which may facilitate cell attachment . Various studies show that direct osteoblast-implant interactions are critical for proper osseointegration. Cell culture models using osteoblastic cells are being commonly used to study bone-biomaterial interface .
In the current study, we examined the proliferation and differentiation characteristics of differentiated C2C12 cells and MC3T3-E1 preosteoblasts on surfaces mimicking the 3M™ESPE™ MDI (test group) and Ankylos® implants. The Ankylos® implant surface was used for comparison as it is a well-established and widely characterized standard implant.
The surfaces of 3M™ESPE™ MDIs are treated to impart roughness which includes sandblasting with aluminum oxide particles, followed by cleaning and passivation with an oxidizing acid . The Ankylos® implant has the FRIADENT plus surface (Dentsply Implants, Mannheim, Germany). It is formed by sandblasting in a temperature-controlled process and acid etching (hydrochloric, sulfuric, hydrofluoric, and oxalic acid) followed by a proprietary neutralizing technique . Considering that both surfaces were sandblasted and acid-treated, we hypothesize that there is no difference in the proliferation and differentiation capacity of osteoblastic cells when cultured on 3M™ESPE™ MDIs and standard implants.
Titanium disks made up with the same materials and surface characteristics as those with the original implants were obtained from the respective manufacturers. Two types of disks were used; the small disks represented 3M™ESPE™ MDI implants, while the large disks represented Ankylos®, Dentsply Friadent implants. A total of 10 disks of each brand were used for the study.
Cell culture and in vitro mineralization
Disks were sterilized and coated with 2% gelatin solution to facilitate the attachment of cells. MC3T3-E1 and C2C12 cells were purchased from ATCC (Manassas, VA, USA). Recombinant human bone morphogenetic protein 2 BMP-2 was purchased from GenScript (Piscataway, NJ, USA). MC3T3-E1 and C2C12 cells were cultured in alpha-MEM (Invitrogen, Carlsbad, CA, USA) and DMEM (Invitrogen, Carlsbad, CA, USA), respectively. Culture media were supplemented with 10% FBS (PAA, Etobocoke, Ontario, Canada) and 100 U/ml penicillin–streptomycin (Invitrogen, Carlsbad, CA, USA). Cells were grown at 37 °C under 5% CO2 in a humidified incubator. Mineralization of MC3T3-E1 cultures was induced by addition of ascorbic acid (50 µg/ml) and sodium phosphate (4 mM) to the culture medium for 12 days.
Cells were fixed with 4% paraformaldehyde. 0.25% calcein (Sigma-Aldrich, Saint Louis, MO, USA), and 2% NaHCO3 solution prepared in 0.15 M NaCl was added to the fixed cells and incubated for 5 min at room temperature. After washing once in PBS, H33258 nuclear staining was performed, washed twice in PBS and images were taken using an inverted fluorescence microscope (EVOS FL, Thermo Fisher Scientific).
In order to examine cellular viability/metabolic activity, Alamar blue solution (Resazurin sodium salt, Sigma-Aldrich, Saint Louis, MO, USA) was directly added to the medium to 100 μM final concentration. The reduction of Alamar blue was measured at 560 nm (reference wavelength 610 nm) after 5-h incubation at 37 °C using a microplate reader (Infinite 200, Tecan).
Generation of BMP2 expressing C2C12 cells
C2C12 cells were electroporated together with 0.4 μg of a BMP-2 expression vector (a kind gift from Dr. Katagiri) and 0.1 μg of pCMV-Tag, which expresses a neomycin-resistance gene. Culture medium was supplemented with 300 μg/ml of G418 (Fisher, Pittsburgh, PA, USA) for 9 days. Clones were picked, amplified, and screened by alkaline phosphatase (ALPL; a downstream target for BMP-2 signaling) staining .
Zymography and Western blotting
Protein samples from the transfected cells were prepared in 1× SDS gel-loading buffer (Laemmli buffer) without adding β-mercaptoethanol and quantified using the Pierce™ Coomassie Plus Assay kit (Thermo Scientific, Rockford, IL, USA). Without heat denaturation, equal amount of protein samples (50 μg) were loaded on a 10% SDS-polyacrylamide gel. After electrophoresis, the gel was incubated in NBT/BCIP (Roche, Mannheim, Germany) staining solution until the bands corresponding to ALPL were clearly visible. Same protein extracts upon heat denaturation in the presence of β-mercaptoethanol were used for Western blotting. The primary antibody used for the analysis was anti-actin (Sigma-Aldrich, Saint Louis, MO, USA). An anti-actin antibody raised in rabbit anti-actin (Sigma-Aldrich, Saint Louis, MO, USA). The secondary antibody was anti-rabbit HRP-IgG (Cell Signaling Technology, Beverly, MA, USA).
Nuclear staining was done by H33258 (Sigma-Aldrich, Saint Louis, MO, USA). After washing in PBS, cells grown on the implants were imaged using an inverted fluorescent microscope (EVOS FL, Thermo Fisher Scientific) and cell nuclei were counted.
Alkaline phosphatase immunostaining and assay
BMP-2-transfected C2C12 cells were fixed in 4% PFA for 15 min, and then blocked with 5% bovine serum albumin (Fisher, Pittsburgh, PA, USA) in Tris buffered saline-0.025%Triton for 30 min at room temperature, followed by overnight incubation with an anti-mouse alkaline phosphatase antibody (R&D systems, Minneapolis, MN, USA). Detection was done by Dylight 488 rabbit anti-goat secondary antibody (Jackson ImmunoResearch, West Grove, PA, USA) with 1-h incubation at room temperature. Fluorescence imaging was performed using an inverted microscope (EVOS FL, Thermo Fisher Scientific). ALPL assay using p-nitrophenyl phosphate was performed as described before .
Scanning electron microscopy
For scanning electron microscopy (SEM), cleaned and sterilized disks in self-sealed pouches were received as such from the respective manufacturers. The disks were carefully mounted on stubs, sputter-coated, and viewed with Carl Zeiss AG-EVO® 40-series scanning electron microscope.
Statistical significance of the differences between the groups was determined using Student’s t test. The statistical power was calculated using the Biomath online software (http://www.biomath.info/power/index.html). We analyzed 10 samples for each group (alpha error 0.05), which resulted in a statistical power of 92%.
Blinding of the investigators
While performing the experiments, JM (first co-author) was not aware of the sources/manufacturers of the disks, which were identified by their size (small and large) only. At the end of the analyses, each disk’s manufacturer was revealed to her by JSD (first co-author).
Ring culture technique
The variable sizes of the implant disks obtained from two different manufacturers demanded an innovative culture system to ensure equal surface areas on both disks for the cell culture experiments. We achieved this by attaching constant diameter (5 mm) plastic cylinders to the disk surface. Disks were sterilized with absolute alcohol, and polystyrene cloning cylinders (Sigma) were attached onto the disks using vacuum grease. The enclosed surfaces on the disks were then coated with sterile 2% gelatin solution (Fig. 1).
Increased surface roughness in the 3M™ESPE™ MDIs
Scanning electron microscopy was used in a secondary electron mode under 10-kV acceleration voltage for producing the images to observe the surface topography, and it showed an increased surface roughness in the 3M™ESPE™ MDIs as compared with Ankylos® (Fig. 2).
Increased proliferation of C2C12 cells grown on 3M™ESPE™ MDI disks
We first examined the proliferation of C2C12 cells treated with BMP-2, a pro-osteogenic cytokine, or without BMP-2 treatment on both types of disks. Ten thousand C2C12 cells were plated, and on the following day, the medium was supplemented with 300 ng/ml of BMP-2. Cells were grown for 3 days, stained with the nuclear stain H33258, and imaged using fluorescence microscopy. Counting of cell nuclei revealed an increased proliferation of the C2C12 cells grown on 3M™ESPE™ MDI disks under both conditions, when treated with BMP-2 or without any treatment (Fig. 3).
Disk type does not affect osteogenic differentiation
C2C12 myoblastic cells were transfected with BMP-2. These cells express high levels of ALPL when compared with the control (untransfected) group (Fig. 4a). ALPL zymography showed a more intense band indicating very high expression of functional ALPL protein in the stably transfected cells (Fig. 4b). The transfected cells were then seeded onto each type of disks (15,000 cells/disk) and were cultured for 3 days. Immunostaining using a goat anti-mouse ALPL antibody revealed a significantly higher number of ALPL-positive cells on the 3M™ESPE™ MDI disks in comparison to those on the Ankylos® disks. Interestingly, when the number of ALPL-positive cells was normalized to the total cell number, no differences were observed. This finding suggests that the increase of ALPL-positive cells was not due to an increased cell differentiation, but because of an increased cell proliferation (Fig. 4c).
Increased proliferation of MC3T3-E1 cells and extracellular matrix mineralization on 3M™ESPE™ MDI disks
Pre-osteoblastic MC3T3-E1 cells were plated on each implant disk (40,000 cells/disk) and were differentiated with mineralization medium for 12 days. Quantification of cells after nuclear staining by H33258 revealed an increased number of cells on the 3M™ESPE™ MDI disks (Fig. 5a). Measurement of cell viability by the reduction of Alamar blue® after 3 days of culture of MC3T3-E1 cells further supported an increase of cell proliferation on the 3M™ESPE™ MDI disks (Fig. 5b).
In order to assess the ability of the system to promote ECM mineralization, MC3T3-E1 cells were plated at equal densities on each disk type and were grown in the presence of differentiation medium for 12 days. Calcein (binds to calcium salts) staining demonstrated an increased mineral deposition on the surface of the 3M™ESPE™ MDI disks when compared with that on the Ankylos® disks. Increased cell proliferation in the 3M™ESPE™ MDI disks cultures may explain the increase in ECM mineralization (Fig. 5c).
In the current study, we used an in vitro cell culture system to evaluate the biocompatibility of two implant materials with different surface topography. Our objective was to establish the osseointegration potential of MDIs versus an established regular implant. Disks prepared from the implant material were coated with gelatin to grow cells, and proliferation and osteogenic differentiation parameters were evaluated. Considering that the disks obtained from two different sources varied in diameter, we attached 5-mm silicon rings to the surface of both types of disks in order to standardize the culture area. The use of vacuum grease created a leak-proof culture well that enabled us to grow and treat cells for the required period of time. Also, it was possible to use a limited number of disks as the system was easy to clean, disinfect, and reuse.
As cells were grown on metallic surfaces, it was not possible to detect them using light microscopy. This is why we used florescence microscopy to examine the cells and their functional properties once the experiment was complete. Considering that we were unable to routinely examine the live cells on the disks during the culture period, we grew the same number of cells under identical conditions on a plastic cell culture dish enclosed by the same type of culture rings. These cells were evaluated daily using an inverted light microscope, and based on the cell density and the amount of mineral precipitation in this latter culture, we decided to terminate the experiments with the cells grown on the disks.
Two different cell lines were used in our in vitro system: C2C12 and MC3T3-E1 cells. Both of these cell lines were developed from mouse tissues. C2C12 cells are myogenic, but retain the potential to express osteogenic markers under appropriate signaling events. Because of their pluripotency, these cells have been considered as a type of mesenchymal stem cells. It has been shown that when treated with BMPs, these cells readily upregulate many key osteoblast markers including RUNX2, OSX, osteocalcin, and alkaline phosphatase (ALPL) . In the current study, we used C2C12 cells that were treated with BMP-2 or stably transfected with a BMP-2 expression vector.
MC3T3-E1 cells have been extensively used in numerous cell culture experiments as a model for osteoblasts . Under differentiating conditions, e.g., in the presence of ascorbic acid and β-glycerol phosphate, these cells upregulate the osteogenic markers and, more importantly, promote the deposition of calcium phosphate minerals within and around the collagen-rich extracellular matrix (ECM). In comparison to BMP2-treated C2C12 cells, MC3T3-E1 cells are considered to be at a more advanced stage of differentiation towards the osteogenic lineage .
Our cell culture system was compatible with both cell types as evident by the outcome of various functional studies, which include cell adherence, synthesis of alkaline phosphatase, and mineralization of the ECM. However, there was a clear difference in the degree of biocompatibility between the two types of implant surfaces; the 3M™ESPE™ MDI showed higher cell numbers and increased deposition of calcium phosphate minerals in comparison to Ankylos®.
The MDI surface was treated with sandblasting and passivation with an oxidizing acid  whereas Ankylos® surface was sandblasted and acid etched . The scanning electron microscopic images showed rougher surface in MDIs in comparison to Ankylos®. The blasting process causes a moderate roughness (1–2 micron) to the implants .
The surface chemistry and topography of biomaterials seem to play an important role in the success or failure upon placement in a biological environment . It has been established that alterations on the surface topography enhance the bone implant contact and biomechanical interaction of the interface during early implantation periods .
MacDonald et al. have shown that wettability, i.e., hydrophilic surfaces support cell interactions and biological fluids better than the hydrophobic surfaces . It has also been shown that roughening the titanium surface improves hydrophilicity . In addition, many authors have stated that rougher surfaces promote differentiation, growth and attachment of bone cells, and higher production of growth factors and augment mineralization [39,40,41,42,43]. However, an in vitro study has demonstrated that osteoblastic cells attach, spread, and proliferate faster on smooth surfaces than on rough surfaces .
ALPL is a late osteogenic marker, which is essential for normal bone mineralization. ALPL-deficient osteoblasts fail to mineralize in culture. Considering that there was no significant difference in the relative ALPL activity in cells grown on two surfaces, it is unlikely that the surface property of the disks affected cell differentiation. This observation does not support the findings of Davies that BMPs, alkaline phosphatase and osteocalcin, the important markers of osteogenic differentiation and bone tissue formation, were express at higher levels on rougher surfaces . In addition to surface topography, surface chemistry is also a very strong variable [46, 47]. Therefore, the different surface chemistry of the implant materials used by Davies and our group might have contributed to this discrepancy. Regardless, there is a general agreement that roughening the implant surface greater than the degree seen by machining only leads to a stronger bone formation as shown in a systematic review .
Our data suggest that the increased cell number is the primary reason why cultures grown on 3M™ESPE™ MDI deposited more minerals in comparison to those grown on Ankylos®. Taken together, we reject the null hypothesis, since our data demonstrates that MDIs have a superior surface quality that promotes cell proliferation, facilitating osseointegration. However, this needs to be tested in vivo.
Our results demonstrate that both implant surfaces are conducive for osteoblastic cell attachment, proliferation, and mineralization. However, 3M™ESPE™ MDI surface shows more pronounced effects on cell proliferation, which may in turn facilitate better osseointegration by enhancing ECM mineralization. Our ongoing research will provide further information on how implant surfaces may affect cell behavior at the implant-tissue interface.
Branemark PI, Hansson BO, Adell R, Breine U, Lindstrom J, Hallen O, et al. Osseointegrated implants in the treatment of the edentulous jaw. Experience from a 10-year period. Scand J Plast Reconstr Surg Suppl. 1977;16:1–132.
Bulard RA, Vance JB. Multi-clinic evaluation using mini-dental implants for long-term denture stabilization: a preliminary biometric evaluation. Compend Contin Educ Dent. 2005;26(12):892–7.
Buchter A, Wiechmann D, Koerdt S, Wiesmann HP, Piffko J, Meyer U. Load-related implant reaction of mini-implants used for orthodontic anchorage. Clin Oral Implants Res. 2005;16(4):473–9.
Fritz U, Diedrich P, Kinzinger G, Al-Said M. The anchorage quality of mini-implants towards translatory and extrusive forces. J Orofac Orthop. 2003;64(4):293–304.
Hong RK, Heo JM, Ha YK. Lever-arm and mini-implant system for anterior torque control during retraction in lingual orthodontic treatment. Angle Orthod. 2005;75(1):129–41.
Mazor Z, Steigmann M, Leshem R, Peleg M. Mini-implants to reconstruct missing teeth in severe ridge deficiency and small interdental space: a 5-year case series. Implant Dent. 2004;13(4):336–41.
Siddiqui AA, Sosovicka M, Goetz M. Use of mini implants for replacement and immediate loading of 2 single-tooth restorations: a clinical case report. J Oral Implantol. 2006;32(2):82–6.
Yeh S, Monaco EA, Buhite RJ. Using transitional implants as fixation screws to stabilize a surgical template for accurate implant placement: a clinical report. J Prosthet Dent. 2005;93(6):509–13.
Kwon KR, Sachdeo A, Weber HP. Achieving immediate function with provisional prostheses after implant placement: a clinical report. J Prosthet Dent. 2005;93(6):514–7.
Ohkubo C, Kobayashi M, Suzuki Y, Sato J, Hosoi T, Kurtz KS. Evaluation of transitional implant stabilized overdentures: a case series report. J Oral Rehabil. 2006;33(6):416–22.
Campelo LD, Camara JR. Flapless implant surgery: a 10-year clinical retrospective analysis. Int J Oral Maxillofac Implants. 2002;17(2):271–6.
Ahn MR, An KM, Choi JH, Sohn DS. Immediate loading with mini dental implants in the fully edentulous mandible. Implant Dent. 2004;13(4):367–72.
Dilek OC, Tezulas E. Treatment of a narrow, single tooth edentulous area with mini-dental implants: a clinical report. Oral Surg Oral Med Oral Pathol Oral Radiol Endod. 2007;103(2):e22–5.
Griffitts TM, Collins CP, Collins PC. Mini dental implants: an adjunct for retention, stability, and comfort for the edentulous patient. Oral Surg Oral Med Oral Pathol Oral Radiol Endod. 2005;100(5):e81–4.
Cooper LF, Zhou Y, Takebe J, Guo J, Abron A, Holmen A, et al. Fluoride modification effects on osteoblast behavior and bone formation at TiO2 grit-blasted c.p. titanium endosseous implants. Biomaterials. 2006;27(6):926–36.
Bachle M, Kohal RJ. A systematic review of the influence of different titanium surfaces on proliferation, differentiation and protein synthesis of osteoblast-like MG63 cells. Clin Oral Implants Res. 2004;15(6):683–92.
Marinucci L, Balloni S, Becchetti E, Belcastro S, Guerra M, Calvitti M, et al. Effect of titanium surface roughness on human osteoblast proliferation and gene expression in vitro. Int J Oral Maxillofac Implants. 2006;21(5):719–25.
Sader MS, Balduino A, Soares Gde A, Borojevic R. Effect of three distinct treatments of titanium surface on osteoblast attachment, proliferation, and differentiation. Clin Oral Implants Res. 2005;16(6):667–75.
Le Guehennec L, Soueidan A, Layrolle P, Amouriq Y. Surface treatments of titanium dental implants for rapid osseointegration. Dent Mater. 2007;23(7):844–54.
Sennerby L, Meredith N. Resonance frequency analysis: measuring implant stability and osseointegration. Compend Contin Educ Dent. 1998;19(5):493–8. 500, 2 ; quiz 4.
Weinstein RL, Francetti L, Sironi R. An analysis of the diagnostic criteria in assessing peri-implant tissues. A critical analysis of the literature. Minerva Stomatol. 1996;45(5):219–26.
Zreiqat H, Valenzuela SM, Nissan BB, Roest R, Knabe C, Radlanski RJ, et al. The effect of surface chemistry modification of titanium alloy on signalling pathways in human osteoblasts. Biomaterials. 2005;26(36):7579–86.
Boyan BD, Hummert TW, Dean DD, Schwartz Z. Role of material surfaces in regulating bone and cartilage cell response. Biomaterials. 1996;17(2):137–46.
Buser D, Broggini N, Wieland M, Schenk RK, Denzer AJ, Cochran DL, et al. Enhanced bone apposition to a chemically modified SLA titanium surface. J Dent Res. 2004;83(7):529–33.
Buser D, Nydegger T, Oxland T, Cochran DL, Schenk RK, Hirt HP, et al. Interface shear strength of titanium implants with a sandblasted and acid-etched surface: a biomechanical study in the maxilla of miniature pigs. J Biomed Mater Res. 1999;45(2):75–83.
Li D, Ferguson SJ, Beutler T, Cochran DL, Sittig C, Hirt HP, et al. Biomechanical comparison of the sandblasted and acid-etched and the machined and acid-etched titanium surface for dental implants. J Biomed Mater Res. 2002;60(2):325–32.
Zhang F, Yang GL, He FM, Zhang LJ, Zhao SF. Cell response of titanium implant with a roughened surface containing titanium hydride: an in vitro study. J Oral Maxillofac Surg. 2010;68(5):1131–9.
Albrektsson T, Wennerberg A. Oral implant surfaces: part 1—review focusing on topographic and chemical properties of different surfaces and in vivo responses to them. Int J Prosthodont. 2004;17(5):536–43.
Ivanoff CJ, Widmark G, Johansson C, Wennerberg A. Histologic evaluation of bone response to oxidized and turned titanium micro-implants in human jawbone. Int J Oral Maxillofac Implants. 2003;18(3):341–8.
Sul YT, Johansson C, Wennerberg A, Cho LR, Chang BS, Albrektsson T. Optimum surface properties of oxidized implants for reinforcement of osseointegration: surface chemistry, oxide thickness, porosity, roughness, and crystal structure. Int J Oral Maxillofac Implants. 2005;20(3):349–59.
Puleo DA, Nanci A. Understanding and controlling the bone-implant interface. Biomaterials. 1999;20(23-24):2311–21.
Cooper LF. Biologic determinants of bone formation for osseointegration: clues for future clinical improvements. J Prosthet Dent. 1998;80(4):439–49.
ESPE M. 3M ESPE MDI Mini Dental Implants [Technical Data Sheet] St. Paul, MN: 3M ESPE Dental Products. 2012. Available at: tinyurlcom/pz3brkq.
Rupp F, Scheideler L, Rehbein D, Axmann D, Geis-Gerstorfer J. Roughness induced dynamic changes of wettability of acid etched titanium implant modifications. Biomaterials. 2004;25(7-8):1429–38.
Li J, Khavandgar Z, Lin SH, Murshed M. Lithium chloride attenuates BMP-2 signaling and inhibits osteogenic differentiation through a novel WNT/GSK3- independent mechanism. Bone. 2011;48(2):321–31.
Sudo H, Kodama HA, Amagai Y, Yamamoto S, Kasai S. In vitro differentiation and calcification in a new clonal osteogenic cell line derived from newborn mouse calvaria. J Cell Biol. 1983;96(1):191–8.
Novaes Jr AB, de Souza SL, de Barros RR, Pereira KK, Iezzi G, Piattelli A. Influence of implant surfaces on osseointegration. Braz Dent J. 2010;21(6):471–81.
MacDonald DE, Markovic B, Allen M, Somasundaran P, Boskey AL. Surface analysis of human plasma fibronectin adsorbed to commercially pure titanium materials. J Biomed Mater Res. 1998;41(1):120–30.
Cooper LF, Masuda T, Yliheikkila PK, Felton DA. Generalizations regarding the process and phenomenon of osseointegration. Part II. In vitro studies. Int J Oral Maxillofac Implants. 1998;13(2):163–74.
Anselme K, Ponche A, Bigerelle M. Relative influence of surface topography and surface chemistry on cell response to bone implant materials. Part 2: biological aspects. Proc Inst Mech Eng H. 2010;224(12):1487–507.
Keller JC, Schneider GB, Stanford CM, Kellogg B. Effects of implant microtopography on osteoblast cell attachment. Implant Dent. 2003;12(2):175–81.
Mustafa K, Wroblewski J, Hultenby K, Lopez BS, Arvidson K. Effects of titanium surfaces blasted with TiO2 particles on the initial attachment of cells derived from human mandibular bone. A scanning electron microscopic and histomorphometric analysis. Clin Oral Implants Res. 2000;11(2):116–28.
Sinha RK, Morris F, Shah SA, Tuan RS. Surface composition of orthopaedic implant metals regulates cell attachment, spreading, and cytoskeletal organization of primary human osteoblasts in vitro. Clin Orthop Relat Res. 1994;305:258–72.
Anselme K, Bigerelle M. Topography effects of pure titanium substrates on human osteoblast long-term adhesion. Acta Biomater. 2005;1(2):211–22.
Davies JE. Mechanisms of endosseous integration. Int J Prosthodont. 1998;11(5):391–401.
Morra M, Cassinelli C, Bruzzone G, Carpi A, Di Santi G, Giardino R, et al. Surface chemistry effects of topographic modification of titanium dental implant surfaces: 1. Surface analysis. Int J Oral Maxillofac Implants. 2003;18(1):40–5.
Cassinelli C, Morra M, Bruzzone G, Carpi A, Di Santi G, Giardino R, et al. Surface chemistry effects of topographic modification of titanium dental implant surfaces: 2. In vitro experiments. Int J Oral Maxillofac Implants. 2003;18(1):46–52.
Wennerberg A, Albrektsson T. Effects of titanium surface topography on bone integration: a systematic review. Clin Oral Implants Res. 2009;20 Suppl 4:172–84.
The authors would like to thank Prof. Georgios Romanos, School of Dental Medicine, Dept. of Periodontology, Stony Brook University, Stony Brook, NY, USA, for his contribution to the study. We would also like to thank 3M ESPE and Dentsply Friadent for providing the implant disks. This work is a part of the thesis submitted by JD for attaining a PhD degree at the Faculty of Dentistry, McGill University, Montreal, Canada.
The funding was received from 3M ESPE for a larger study to establish the osseointegration potential of the 3M™ESPE™ MDI for building a scientific evidence. Authors had no commercial interest involved. The comparator implant disks were obtained from Dentsply Friadent for research and comparison purpose only.
JM carried out the cell cultures experiments, analyzed the data, and drafted the manuscript. JSD conceived the study and drafted the manuscript. SA established the in vitro culture system. JL generated and characterized the BMP-2-transfected cell line. JSF participated in designing the study. MM provided lab support, designed and coordinated the study, analyzed the data, and drafted the final version of the manuscript. All authors read and approved the final manuscript.
Jagjit Singh Dhaliwal, Juliana Marulanda, JingJing Li, Sharifa Alebrahim, Jocelyne S. Feine, and Monzur Murshed declare that they have no competing interests in the manuscript.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Dhaliwal, J.S., Marulanda, J., Li, J. et al. In vitro comparison of two titanium dental implant surface treatments: 3M™ESPE™ MDIs versus Ankylos®. Int J Implant Dent 3, 27 (2017) doi:10.1186/s40729-017-0083-5